Thread: plastic lens vs glass lens for prototyping and low volume custom lenses

  1. #1

    Default plastic lens vs glass lens for prototyping and low volume custom lenses

    I don't wish to start a heated debate here over glass vs acrylic/pc and I'm sure people here and elsewhere have discussed all there is to pros and cons of each. But as I am not as skilled in optics as well as other related fields the information is hard for me to consume, so I hope to ask few questions here and have a friendly conversation and learn, nothing more.

    From what I have read, the transmittance of typical glass is 90% while acrylic is 92%. But this doesn't take into account the type of glass, type of plastic (pet, pcarb, acrylic), the optical finish quality, AR coatings.
    My question is, typically, given a typical average AR coated acrylic glass or lens and similar glass one, can we assume likely that they will have the same light transmittance? If not, which one will be better, how much and why?

    Refractive index is better for glass which allows thinner lenses for same results. Is this a good rule of thumb or is there more to it worth knowing?
    If this is the case, why are plastic lenses a thing? I understand plastic is less likely to shutter but it's used in places where there is not much need for that. Is plastic just easier to mold/machine with cheaper tools? If so, why is glass used for expensive lenses where few grams wouldn't change much?

    My goal is to find out the most affordable way to get prototype and low volume custom lenses made, with as little sacrifice to quality as possible.
    My current impression is acrylic is better for this purpose as its cheaper to mold and transmittance and lens properties are very close to glass and things get different with expensive high optical grade glass. But I may be totally wrong. As for polycarbonate vs acrylic for windows and lenses I managed to find even less info.

    PS: I am aware plastic can melt with high power laser beams.

  2. #2
    Join Date
    Jun 2009
    Location
    St. Louis, MO
    Posts
    558

    Default

    Prototyping implies NOT making incredibly expensive molds to produce small quantities of lenses. Plastic lenses change their shape while cooling which implies controlling your process very carefully to achieve predictable results. There are a whole lot of different glasses - each with differering index of refraction and dispersion available. Dispersion (often referred to the Abbe number) and index refraction are how optical materials are specified. Back in the bad old days Abbe mined Calcium Fluorite to combine with normal glasses to make the first Apochromatic microscope objectives at Zeiss. He and Carl Zeiss invested in the startup of Schott Glass because having more glass options was important to getting where they wanted to go at Zeiss. The lasers we use for light shows today are essentially a single color it's possible to do a lot with a single lens - that's not the norm in optical design.
    "There are painters who transform the sun into a yellow spot, but there are others who, with the help of their art and their intelligence, transform a yellow spot into the sun." Pablo Picasso

  3. #3
    Join Date
    Nov 2008
    Location
    Cleveland Ohio
    Posts
    1,528

    Default

    Can you 3d print a good lens yet? I doubt you can do normal ones but I bet you can do a fresnel using the liquid /laser type of printing. SLS. I think it is called. Can you yet print in glass and have it transmit light well?

    Sorry not you question. I’ve seen some plastic out perform glass and the other way too for laser. I think given the high power today the question is more about damage to the optic then the ability of the optic. Coatings are very important.

    If you below watt. Non of this much matters.

  4. #4
    Join Date
    May 2007
    Location
    Authentic Asian food area of SoCal
    Posts
    2,279

    Default

    Quote Originally Posted by kecked View Post
    Can you 3d print a good lens yet? I doubt you can do normal ones but I bet you can do a fresnel using the liquid /laser type of printing. ...
    SLA printers *can* do it but the resins are not of optical quality and there would most likely be some post process grinding/shaping needed. Also, since these resins are photopolymers, they would be completely useless at 405nm and probably extremely lossy up to 450nm. So really, only red would be "usable" and even then, I doubt it.

  5. #5

    Default

    Quote Originally Posted by laserist View Post
    Prototyping implies NOT making incredibly expensive molds to produce small quantities of lenses.
    Yes, but what options do I have for few prototype designs and then 10-100 custom lenses of the final design?
    I think precision milling 100 or even just 10 acrylic lenses will cost more than milling one aluminum block and injecting acrylic into it 10 times. Am I wrong?

    Plastic lenses change their shape while cooling which implies controlling your process very carefully to achieve predictable results.
    I was thinking of getting a mold and injection molding done by a 3rd party service rather than myself.
    There are some bench <1000 USD injection molding machines but I don't know how well they would work for lenses.
    https://www.youtube.com/watch?v=uD-kCf8amHk

    Plus I have access to a friend's professional CNC miller that can mill aluminum and steel. He can also let me use of his injection molding machine which his small company uses for making plastic toys.
    But whether these are precise enough I don't know. Are plastic optical molds made with specialized high precision CNCs and injection molding machines? Or should I check for some values in the spec sheets and give it a try if certain requirements are met?

    Plastic lenses change their shape while cooling which implies controlling your process very carefully to achieve predictable results.
    If the lens remains in the mold while cooling as well? If so, yes that might be a problem.

    I hope there are some online services that can do this as well. But I also hope they won't charge me my kidney.
    With general 3d printing and mold making Shapeways.com has been very affordable and good to me. But for metal they do manual polishing after printing the wax and casting the metal.


    Quote Originally Posted by kecked View Post
    Can you 3d print a good lens yet? I doubt you can do normal ones but I bet you can do a fresnel using the liquid /laser type of printing. SLS. I think it is called. Can you yet print in glass and have it transmit light well?
    In my experience even the best 3d printers and general purpose CNC machines produce a result with too much roughness that needs to be sanded then polished to be usable. Since the polishing is done by hand its not very precise. For fun optical illusion projects it seems more than enough ,but for prototyping optical design it is unreliable.
    Quote Originally Posted by kecked View Post
    Can you yet print in glass and have it transmit light well?
    Some researchers are working on decent quality glass 3d printers but nothing more than claims so far.

  6. #6
    Join Date
    Nov 2008
    Location
    Cleveland Ohio
    Posts
    1,528

    Default

    Thanks for the info. It would be truly a game changer to be able to make our own high quality lenses.

  7. #7
    Join Date
    Aug 2008
    Location
    UK
    Posts
    5,642

    Default

    Quote Originally Posted by aku View Post

    From what I have read, the transmittance of typical glass is 90% while acrylic is 92%. But this doesn't take into account the type of glass, type of plastic (pet, pcarb, acrylic), the optical finish quality, AR coatings.
    My question is, typically, given a typical average AR coated acrylic glass or lens and similar glass one, can we assume likely that they will have the same light transmittance? If not, which one will be better, how much and why?
    Low iron glass such as Pilkington Optiwhite has a transmittance of 92%.